蒸煮型聚丙烯流延膜芯层专用料的开发

浏览(155) 下载(6)

作者单位:: 中国石油化工股份有限公司茂名分公司研究院，广东茂名 525000
Sinopec Maoming Petrochemical Company Research Institute，Maoming 525000，China

关键词:: 聚丙烯流延膜；抗粘；芯层；无机纳米助剂
CPP；anti-viscosity；core layer；inorganic nanometer additive

摘要:: 摘要：根据市场主流牌号分析，确定蒸煮型聚丙烯流延膜芯层专用料的开发目标。筛选出芯

层专用的球形无机纳米复合助剂C（添加量为0.04%），在茂名石化国产2代聚丙烯装置成功生

产出蒸煮型流延膜芯层专用聚丙烯树脂PPR-F08M-S，并对产品物性进行分析和加工应用试

验，结果表明：树脂黄色指数为-4.62，拉伸强度达到29.4 MPa，弯曲模量为791 MPa，薄膜雾度

为0.82%，薄膜制品综合性能较好，与进口树脂性能相当。

Abstract: According to the analysis of the mainstream brand of the market, the development target of the special material for RCPP

core layer was determined. A special spherical inorganic nano-composite agent C (adding 0.04%) for the core layer was screened

out. PPR-F08M-S, a special polypropylene resin for the core layer of casting film, was successfully produced in the 2nd generation

polypropylene plant made in Maoming Petrochemical Company. The physical properties of the product were analyzed and processed.

The results showed that, the yellow index of the resin was -4.62, the tensile strength was 29.4MPa, the bending modulus was 791

MPa, and the fog degree of the film was 0.82%. The comprehensive properties of the film products were better and were equal to that

of the imported resin.